K129 Epoxy Resin Infusion Foam Core
The K129 belongs to resin infusion foam core, it can be foamed in any shape with mold. When it combines with resin and carbon fiber, it will become a composite product like carbon fiber paddle blade, composite plate, carbon board, and so on. And this process about the use of the foam called HEM, welcome to click the link to know more the HEM process.
Resin Infusion Foam Core Specification
- Item: K129
- Density Type: Medium
- Theoretical Foaming Ratio@1atm 150℃ 20Min: 8.5Times
- Practical Foaming Ratio: 1.2Times
- Initial Density: 0.3 g/cm 3
- Foaming Density: 0.15 – 0.35 g/cm 3
- Hardness: Shore C: >=95
- Main Applications: Composite Board & Blade
- Foaming Process: HEM1, can be produced in many complicated shape
- Description
- Technical
- Custom
- Reviews (0)
Description
Introducing the K129 resin infusion foam core, a high-performance, medium-density foam solution designed for a variety of advanced composite applications. With a theoretical foaming ratio of 8.5 times at 1 atm and 150°C over 20 minutes, the K129 delivers exceptional versatility in form and function, allowing for intricate designs and custom shapes through the HEM1 foaming process.
Meanwhile, K129 resin infusion foam core is engineered to provide optimal stiffness while remaining lightweight, making it an ideal choice for composite boards and paddle blades. Its superior hardness and density characteristics ensure durability and performance in demanding environments. Whether you are looking to enhance your sporting goods or innovate in composite manufacturing, the K129 Foam Core is your go-to solution for achieving the perfect balance of strength and weight.
For more composite foamcores, please contact us for more details.
Technical Characteristic
| Weight | 125±10g（Not including packing material） |
| Size | L：600±5mm；W：300±5mm；T：2.5±0.5mm |
| Intial Density | 0.30±0.05g/cm 3 |
| Foaming Temperature | 130℃-160℃（Suggest to 150℃ will be better） |
| Theeoretical Foaming Ratio | 6-11Times @1atm，150℃， |
| Practical Foaming Ratio | 1-15Times，0.25-0.30g/cm 3 |
| Foaming Hardness | Shore A：80-90@ρ=0.25g/cm 3 ，145℃，50min |
| High Temperature Resistance | 80℃ 2h Heating less than 1.0% @ρ=0.25g/cm 3 ，145℃，50min |
| Mechanical Properties at Room Temperature @ρ=0.25g/cm 3
| GB/T1448-2005 | Strength of Compression / MPa | 3.5 |
| Modulus of Compression / MPa | 44.62 | ||
| GB/T1449-2005 | Strength of Flexural / MPa | 8.52 | |
| Modulus of Flexural / MPa | 285.05 | ||
| GB/T1447-2005 | Strength of Tensile / MPa | 3.21 | |
| Modulus of Tensile / MPa | 27.45 | ||
| Percentage of Breaking Elongation / % | 7.45 | ||
| GB/T1455-2005 | Strength of Cutting / MPa | 0.68 | |
| Modulus of Cutting / MPa | 2.54 |
Customized Foams & Products
For this epoxy foam core material, we can assist our customers in resolving many issues.
Firstly, we can adjust and customize the core material’s color, density, hardness, and other specifications based on the customer’s requirements.
Secondly, we can process the core into your desired shape through mold creation or CNC machining.